Preparation of diamond-like carbon films by double cathodes pulse glow discharge plasma vapor deposition
Fazhan Yang  1, 2@  , Liru Shen  1@  , Shiqing Wang  1, 2@  , Haifeng Liu  1, 2@  , Fanya Jin  1@  
1 : Southwestern Institute of Physics
Chengdu 6100 -  China
2 : The Engineering & technical College of Chengdu University of Technology
Leshan 614000 -  China

Hydrogenated diamond-like carbon (DLC) films were deposited on silicon chip by double cathodes pulse glow discharge plasma vapor deposition at different gas flow rates. The surface morphology,composition and microstructure of films was observed by atomic force microscope(AFM), X-ray photoelectron spectroscope(XPS)and spectroscopy Raman spectrometer. The Raman spectra of a -C : Hs show different trends. It was found that different systems exhibit different positions of G peak, D peak, G peak full width at half maximum (FWHM(G) ), as well as different I (D)/I (G) values and sp3 bond content . In one case, When H2:Ar:C2H2 gas volume ratio is from 4:1:1 to 8:1:1, the positions of G peak and D peak are slightly upwardthe , I (D)/I (G) values decrease with increasing sp3bond content, In the second case, both sp3 bond content with FWHM(G) have the different trends are found,they do not have a consistent linear relationship .



  • Other
Online user: 1 RSS Feed